2018 New Style Low Carbon Steel Shot S460 - Low Carbon Steel Shot – TAA
2018 New Style Low Carbon Steel Shot S460 - Low Carbon Steel Shot – TAA Detail:
Product feature
High strengthen, high tenacity, long service life.
Low breakage, low dust, low pollution.
Low wear of the equipments, long life of accessory.
Reduce dedusting system load, lengthen usage time of dedusting equipments.
Technical specification
|
Chemical Composition% |
C |
0.10-0.20% |
|
Si |
0.10-0.35% |
|
|
Mn |
0.35-1.50% |
|
|
S |
≤0.05% |
|
|
P |
≤0.05% |
|
|
Other alloy elements |
Adding Cr Mo Ni B Al Cu etc. |
|
|
Hardness |
HRC42-48/48-54 |
|
|
Microstructure |
Duplex structure combined Martensite and Bainite |
|
|
Density |
≥ 7.2g/cm3 |
|
|
External form |
Spherical |
|
Size distribution
| Screen No. | Inch | Screen size | S70 | S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
| 6 | 0.132 | 3.35 | All pass | |||||||||||
| 7 | 0.111 | 2.80 | All pass | |||||||||||
| 8 | 0.0937 | 2.36 | All pass | ≥90% | ||||||||||
| 10 | 0.0787 | 2.00 | All pass | All pass | ≥85% | ≥97% | ||||||||
| 12 | 0.0661 | 1.70 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 14 | 0.0555 | 1.40 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 16 | 0.0469 | 1.18 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 18 | 0.0394 | 1.00 | All pass | ≤5% | ≥85% | ≥96% | ||||||||
| 20 | 0.0331 | 0.850 | All pass | ≤10% | ≥85% | ≥96% | ||||||||
| 25 | 0.0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
| 30 | 0.0232 | 0.600 | All pass | ≥85% | ≥96% | |||||||||
| 35 | 0.0197 | 0.500 | ≤10% | ≥97% | ||||||||||
| 40 | 0.0165 | 0.425 | All Pass | ≥85% | ||||||||||
| 45 | 0.0138 | 0.355 | ≤10% | ≥97% | ||||||||||
| 50 | 0.0117 | 0.300 | ≥80% | |||||||||||
| 80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
| 120 | 0.0049 | 0.125 | ≥90% | |||||||||||
| 200 | 0.0029 | 0.075 |
Fatigue Life Test
Consumption Contrast Figure of TAA LCB steel shot, low-carbon steel shot and high-carbon steel shot.(fatigue life test of normal grades at an impacting speed ratio of 60.96m/s)
Consumption contrast-Normal grade
Through the fatigue life test we can see that: the service life of TAA LCB Steel Shot is 1.5 times longer than common low carbon steel shot, 2 times longer than high carbon steel shot.
Application
Blast cleaning: Used for blast cleaning of casting, die-casting, forging; sand removal of casting, steel plate, H type steel, steel structure.
Rust removal: Rust removal of casting, forging, steel plate, H type steel, steel structure.
Shot peening: Shot peening of gear, heat treated parts.
Sand blasting: Sand blasting of profile steel, ship board, steel board, steel material, steel structure.
Pre-treatment: Pre-treatment of surface, steel board, profile steel, steel structure, before painting or coating.
Product detail pictures:
Related Product Guide:
To regularly increase the management program by virtue from the rule of "sincerely, good religion and high quality are the base of enterprise development", we greatly absorb the essence of linked products internationally, and constantly produce new goods to satisfy the calls for of shoppers for 2018 New Style Low Carbon Steel Shot S460 - Low Carbon Steel Shot – TAA , The product will supply to all over the world, such as: Bangladesh, United States, Houston, Our company always concentrate on the development of the international market. We now have a lot of customers in Russia , European countries, the USA, the Middle East countries and Africa countries. We always follow that quality is foundation while service is guarantee to meet all customers.
By Heloise from Johannesburg - 2018.12.14 15:26
The customer service staff is very patient and has a positive and progressive attitude to our interest, so that we can have a comprehensive understanding of the product and finally we reached an agreement, thanks!
By Dale from Orlando - 2018.11.06 10:04
Related products
-
Best Price for Cutting Disc 4.5inch - Grinding...
Our super-hard alloy tools are produced by brazing. Under certain conditions, a layer of diamond is firmly welded to the metal substrate after a metal solder melting process. This type of product has the characteristics of high grinding efficiency, long service life, safety, environmental protection and pollution-free. Mainly replace the current resin bond corundum cutting and polishing tools, all coarse and medium coarse-grained electroplated diamond tools, and some hot-pressed sintered diam...
-
Quality Inspection for 1200 Brown Fused Aluminu...
Compared with traditional steel grit made by crushing steel shot, bearing steel grit has the following Features: Raw Material Bearing steel grit is made by Chromium bearing steel which has good harden ability due to its high content of Chromium. Technology Bearing steel grit is made by crushing the forged bearing steel directly which is free from casting defects. Low wear The forged state bearing steel grit with sharp edges has higher mechanical property than traditional cast steel grit with...
-
Best quality Garnet 80 Mesh Prices - Stainless...
Stainless steel cut wire shot is widely used for the shot/air blasting of various types of non-ferrous metal castings, stainless steel products, aluminum parts, hardware tools, natural stone, etc, highlighting the metal color and achieving smooth, rust-free, matt fi nishing surface treatment eff ect. With good quality stainless steel wire raw material, stainless steel shot is featured with uniform particles and hardness, which guarantees its long service life and good blasting eff ect. The pe...
-
OEM China 80# Sponge Media Abrasives - Copper ...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass b...
-
Massive Selection for Brown Fused Alumina Uses ...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass beads 5. Sh...
-
China Cheap price Hook Shot Blasting Machine -...
TAA high performance blast wheel have proven themselves on the market to be robust, economically efficient and maintenance-friendly. They are available with different turbine wheel diameters and a variety of spare and wear materials (e. g. hard metal). TAA high performance blast wheels are very popular for modernizing conventional shot-blasting machines as well. Product Features Improving shot blasting speed obviously Good wear resistance Reducing energy consumption greatly Extraordinary serv...