High Quality Stainless Steel Polishing Shot - Low Carbon Steel Shot – TAA
High Quality Stainless Steel Polishing Shot - Low Carbon Steel Shot – TAA Detail:
Product feature
High strengthen, high tenacity, long service life.
Low breakage, low dust, low pollution.
Low wear of the equipments, long life of accessory.
Reduce dedusting system load, lengthen usage time of dedusting equipments.
Technical specification
|
Chemical Composition% |
C |
0.10-0.20% |
|
Si |
0.10-0.35% |
|
|
Mn |
0.35-1.50% |
|
|
S |
≤0.05% |
|
|
P |
≤0.05% |
|
|
Other alloy elements |
Adding Cr Mo Ni B Al Cu etc. |
|
|
Hardness |
HRC42-48/48-54 |
|
|
Microstructure |
Duplex structure combined Martensite and Bainite |
|
|
Density |
≥ 7.2g/cm3 |
|
|
External form |
Spherical |
|
Size distribution
| Screen No. | Inch | Screen size | S70 | S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
| 6 | 0.132 | 3.35 | All pass | |||||||||||
| 7 | 0.111 | 2.80 | All pass | |||||||||||
| 8 | 0.0937 | 2.36 | All pass | ≥90% | ||||||||||
| 10 | 0.0787 | 2.00 | All pass | All pass | ≥85% | ≥97% | ||||||||
| 12 | 0.0661 | 1.70 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 14 | 0.0555 | 1.40 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 16 | 0.0469 | 1.18 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 18 | 0.0394 | 1.00 | All pass | ≤5% | ≥85% | ≥96% | ||||||||
| 20 | 0.0331 | 0.850 | All pass | ≤10% | ≥85% | ≥96% | ||||||||
| 25 | 0.0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
| 30 | 0.0232 | 0.600 | All pass | ≥85% | ≥96% | |||||||||
| 35 | 0.0197 | 0.500 | ≤10% | ≥97% | ||||||||||
| 40 | 0.0165 | 0.425 | All Pass | ≥85% | ||||||||||
| 45 | 0.0138 | 0.355 | ≤10% | ≥97% | ||||||||||
| 50 | 0.0117 | 0.300 | ≥80% | |||||||||||
| 80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
| 120 | 0.0049 | 0.125 | ≥90% | |||||||||||
| 200 | 0.0029 | 0.075 |
Fatigue Life Test
Consumption Contrast Figure of TAA LCB steel shot, low-carbon steel shot and high-carbon steel shot.(fatigue life test of normal grades at an impacting speed ratio of 60.96m/s)
Consumption contrast-Normal grade
Through the fatigue life test we can see that: the service life of TAA LCB Steel Shot is 1.5 times longer than common low carbon steel shot, 2 times longer than high carbon steel shot.
Application
Blast cleaning: Used for blast cleaning of casting, die-casting, forging; sand removal of casting, steel plate, H type steel, steel structure.
Rust removal: Rust removal of casting, forging, steel plate, H type steel, steel structure.
Shot peening: Shot peening of gear, heat treated parts.
Sand blasting: Sand blasting of profile steel, ship board, steel board, steel material, steel structure.
Pre-treatment: Pre-treatment of surface, steel board, profile steel, steel structure, before painting or coating.
Product detail pictures:
Related Product Guide:
Our primary objective is usually to offer our shoppers a serious and responsible small business relationship, offering personalized attention to all of them for High Quality Stainless Steel Polishing Shot - Low Carbon Steel Shot – TAA , The product will supply to all over the world, such as: Tanzania, Washington, Myanmar, We adopt advanced production equipment and technology, and perfect testing equipment and methods to ensure our product quality. With our high-level talents, scientific management, excellent teams, and attentive service, our products are favored by domestic and foreign customers. With your support, we will build a better tomorrow!
By Sara from luzern - 2018.09.29 13:24
The customer service staff's answer is very meticulous, the most important is that the product quality is very good, and packaged carefully, shipped quickly!
By Adam from Karachi - 2017.07.28 15:46
Related products
-
Cheapest Factory 80# Glass Beads - Copper cut ...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass b...
-
PriceList for Steel Grit Gp18 - Zinc cut wire ...
Made from high grade zinc wire, produced by cutting zinc wire into pellets, the length equal to the diameter of the wire. Zinc Cut Wire is also available in a conditioned form which is used as a longer lasting alternative to cast zinc shot. These are ideal for deflashing and finishing die castings, normally in wheel blast equipment. Available at competent rates, our products reduce wear and tear on blast equipment compared to most other metallic abrasives. Features 1. Bright colour and lustre...
-
Big discounting Side Guard Plate - Steel Mill ...
Steel mill tumble belt shot blast machines are used for deburring,descaling, sand removal and derusting mass parts. They are operated either as a stand-alone solution or as part of a line. In addition to the standard program, delivers this machine in several sizes and designs. The machines are equipped with the tried and tested high-performance turbines and the maintenance-friendly cartridge filter systems. Decisive Advantages of Steel mill tumble belt shot blast machines: AGTOS Blasting tech...
-
Factory made hot-sale Diamond Cutting Disk - C...
Our super-hard alloy tools are produced by brazing. Under certain conditions, a layer of diamond is firmly welded to the metal substrate after a metal solder melting process. This type of product has the characteristics of high grinding efficiency, long service life, safety, environmental protection and pollution-free. Mainly replace the current resin bond corundum cutting and polishing tools, all coarse and medium coarse-grained electroplated diamond tools, and some hot-pressed sintered diam...
-
OEM/ODM Supplier Garnet For Waterjet Cutting -...
Made from high grade zinc wire, produced by cutting zinc wire into pellets, the length equal to the diameter of the wire. Zinc Cut Wire is also available in a conditioned form which is used as a longer lasting alternative to cast zinc shot. These are ideal for deflashing and finishing die castings, normally in wheel blast equipment. Available at competent rates, our products reduce wear and tear on blast equipment compared to most other metallic abrasives. Features 1. Bright colour and lustre...
-
Free sample for Steel Cutting Disc - Cutting d...
Our super-hard alloy tools are produced by brazing. Under certain conditions, a layer of diamond is firmly welded to the metal substrate after a metal solder melting process. This type of product has the characteristics of high grinding efficiency, long service life, safety, environmental protection and pollution-free. Mainly replace the current resin bond corundum cutting and polishing tools, all coarse and medium coarse-grained electroplated diamond tools, and some hot-pressed sintered diam...