Popular Design for Sponge Blasting Media - Low Carbon Steel Shot – TAA
Popular Design for Sponge Blasting Media - Low Carbon Steel Shot – TAA Detail:
Product feature
High strengthen, high tenacity, long service life.
Low breakage, low dust, low pollution.
Low wear of the equipments, long life of accessory.
Reduce dedusting system load, lengthen usage time of dedusting equipments.
Technical specification
|
Chemical Composition% |
C |
0.10-0.20% |
|
Si |
0.10-0.35% |
|
|
Mn |
0.35-1.50% |
|
|
S |
≤0.05% |
|
|
P |
≤0.05% |
|
|
Other alloy elements |
Adding Cr Mo Ni B Al Cu etc. |
|
|
Hardness |
HRC42-48/48-54 |
|
|
Microstructure |
Duplex structure combined Martensite and Bainite |
|
|
Density |
≥ 7.2g/cm3 |
|
|
External form |
Spherical |
|
Size distribution
| Screen No. | Inch | Screen size | S70 | S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
| 6 | 0.132 | 3.35 | All pass | |||||||||||
| 7 | 0.111 | 2.80 | All pass | |||||||||||
| 8 | 0.0937 | 2.36 | All pass | ≥90% | ||||||||||
| 10 | 0.0787 | 2.00 | All pass | All pass | ≥85% | ≥97% | ||||||||
| 12 | 0.0661 | 1.70 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 14 | 0.0555 | 1.40 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 16 | 0.0469 | 1.18 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 18 | 0.0394 | 1.00 | All pass | ≤5% | ≥85% | ≥96% | ||||||||
| 20 | 0.0331 | 0.850 | All pass | ≤10% | ≥85% | ≥96% | ||||||||
| 25 | 0.0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
| 30 | 0.0232 | 0.600 | All pass | ≥85% | ≥96% | |||||||||
| 35 | 0.0197 | 0.500 | ≤10% | ≥97% | ||||||||||
| 40 | 0.0165 | 0.425 | All Pass | ≥85% | ||||||||||
| 45 | 0.0138 | 0.355 | ≤10% | ≥97% | ||||||||||
| 50 | 0.0117 | 0.300 | ≥80% | |||||||||||
| 80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
| 120 | 0.0049 | 0.125 | ≥90% | |||||||||||
| 200 | 0.0029 | 0.075 |
Fatigue Life Test
Consumption Contrast Figure of TAA LCB steel shot, low-carbon steel shot and high-carbon steel shot.(fatigue life test of normal grades at an impacting speed ratio of 60.96m/s)
Consumption contrast-Normal grade
Through the fatigue life test we can see that: the service life of TAA LCB Steel Shot is 1.5 times longer than common low carbon steel shot, 2 times longer than high carbon steel shot.
Application
Blast cleaning: Used for blast cleaning of casting, die-casting, forging; sand removal of casting, steel plate, H type steel, steel structure.
Rust removal: Rust removal of casting, forging, steel plate, H type steel, steel structure.
Shot peening: Shot peening of gear, heat treated parts.
Sand blasting: Sand blasting of profile steel, ship board, steel board, steel material, steel structure.
Pre-treatment: Pre-treatment of surface, steel board, profile steel, steel structure, before painting or coating.
Product detail pictures:
Related Product Guide:
Good quality comes to start with; service is foremost; organization is cooperation" is our enterprise philosophy which is regularly observed and pursued by our firm for Popular Design for Sponge Blasting Media - Low Carbon Steel Shot – TAA , The product will supply to all over the world, such as: Albania, Iran, Algeria, We offer the great variety of products in this field. Besides, customized orders are also available. What's more, you will enjoy our excellent services. In one word, your satisfaction is guaranteed. Welcome to visit our company! For more information, please come to our website.If any further inquiries, please feel free to contact us.
By Alberta from London - 2018.04.25 16:46
It is really lucky to meet such a good supplier, this is our most satisfied cooperation, I think we will work again!
By Madge from Iran - 2018.09.19 18:37
Related products
-
Good Quality Diamond Cutting Disc For Tiles - ...
Our super-hard alloy tools are produced by brazing. Under certain conditions, a layer of diamond is firmly welded to the metal substrate after a metal solder melting process. This type of product has the characteristics of high grinding efficiency, long service life, safety, environmental protection and pollution-free. Mainly replace the current resin bond corundum cutting and polishing tools, all coarse and medium coarse-grained electroplated diamond tools, and some hot-pressed sintered diam...
-
Newly Arrival Aluminum Cut Wire 2.5mm - Bearin...
Compared with traditional steel grit made by crushing steel shot, bearing steel grit has the following Features: Raw Material Bearing steel grit is made by Chromium bearing steel which has good harden ability due to its high content of Chromium. Technology Bearing steel grit is made by crushing the forged bearing steel directly which is free from casting defects. Low wear The forged state bearing steel grit with sharp edges has higher mechanical property than traditional cast steel grit with...
-
Hot sale Steel Grit Gp40 - Garnet – TAA
Features ■ Low Dust—The high intrinsic tenacity and a high proportion of the material itself fast the settlement rate and significantly reduce the dust emissions and dust coming from the workpiece, minimizing cleaning effort sandblasting, reducing pollution of the work area. ■ Excellent Surface Quality—It can deep into the voids and uneven parts to clean, thereby completely remove rust, soluble salts and other contaminants; surface blasting process without inserts, will not advers...
-
factory customized Tone Garnet Sand - Zinc cut...
Made from high grade zinc wire, produced by cutting zinc wire into pellets, the length equal to the diameter of the wire. Zinc Cut Wire is also available in a conditioned form which is used as a longer lasting alternative to cast zinc shot. These are ideal for deflashing and finishing die castings, normally in wheel blast equipment. Available at competent rates, our products reduce wear and tear on blast equipment compared to most other metallic abrasives. Features 1. Bright colour and lustre...
-
Quality Inspection for 410 Stainless Steel Cut ...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass beads 5. Sh...
-
Hot sale Factory Concrete Protective Liner - R...
Advantages of AGTOS rubber belt tumble blast machines Reliable blasting technology Innovative filter technology Many different variants Automation through harmonisation with in-house transport system. AGTOS high-performance turbines: Our turbines are solid, well-constructed pieces of machinery. Due to a smaller number of wear parts and high abrasive throughput, they operate extremely economically. Many different variants: Because of the many different variants, it is possible to build the opt...