Steel Grit
Available Hardness:
GP: HRC46-50
Newly made products with angular, the grit are gradually rounded off in use and its particularly suited for oxide skin pre-treatment.
GL: HRC56-60
Harder than GP steel grit, also loses its sharp edges during shot basting and is particularly suited to surface preparation applications.
GH: HRC63-65
High hardness, sharp edges remain during operation, mainly used for compressed air shot blasting equipment.
Production Strength:
TAA adopts Arc Furnace Smelting and Double Quenching technology, which guarantee its metal abrasives' chemical composition and high strength, high tenacity, long service life.
Tech Data: Steel Grit
|
Chemical Composition% |
C |
0.85-1.2 |
|
Si |
0.40-1.2 |
|
|
Mn |
0.60-1.2 |
|
|
S |
≤0.050 |
|
|
P |
≤0.050 |
|
|
Hardness |
GP |
HRC 46-50 |
|
GL |
HRC 53-60 |
|
|
GH |
HRC 63-65 |
|
|
Density |
≥7.4 g/cm3 |
|
|
microstructure |
Homogeneous tempered martensite or Troostite |
|
|
Appearance |
Angular |
|
Size distribution
|
Screen No. |
In |
Screen Size |
SAE J444 |
|||||||||
|
G10 |
G12 |
G14 |
G16 |
G18 |
G25 |
G40 |
G50 |
G80 |
G120 |
|||
|
6 |
0.132 |
3.35 |
|
|
|
|
|
|
|
|
|
|
|
7 |
0.111 |
2.80 |
All Pass |
|
|
|
|
|
|
|
|
|
|
8 |
0.0937 |
2.36 |
|
All Pass |
|
|
|
|
|
|
|
|
|
10 |
0.0787 |
2.00 |
≥80% |
|
All Pass |
|
|
|
|
|
|
|
|
12 |
0.0661 |
1.70 |
≥90% |
≥80% |
|
All Pass |
|
|
|
|
|
|
|
14 |
0.0555 |
1.40 |
|
≥90% |
≥80% |
|
All Pass |
|
|
|
|
|
|
16 |
0.0469 |
1.18 |
|
|
≥90% |
≥75% |
|
All Pass |
|
|
|
|
|
18 |
0.0394 |
1.00 |
|
|
|
≥85% |
≥75% |
|
All |
|
|
|
|
20 |
0.0331 |
0.850 |
|
|
|
|
|
|
|
|
|
|
|
25 |
0.0280 |
0.710 |
|
|
|
|
≥85% |
≥70% |
|
All Pass |
|
|
|
30 |
0.0232 |
0.600 |
|
|
|
|
|
|
|
|
|
|
|
35 |
0.0197 |
0.500 |
|
|
|
|
|
|
|
|
|
|
|
40 |
0.0165 |
0.425 |
|
|
|
|
|
≥80% |
≥70% |
|
All Pass |
|
|
45 |
0.0138 |
0.355 |
|
|
|
|
|
|
|
|
|
|
|
50 |
0.0117 |
0.300 |
|
|
|
|
|
|
≥80% |
≥65% |
|
All Pass |
|
80 |
0.007 |
0.180 |
|
|
|
|
|
|
|
≥75% |
≥65% |
|
|
120 |
0.0049 |
0.125 |
|
|
|
|
|
|
|
|
≥75% |
≥60% |
|
200 |
0.0029 |
0.075 |
|
|
|
|
|
|
|
|
|
≥75% |
Application
Blast cleaning: Used for blast cleaning of casting, die-casting, forging; sand removal of casting, steel plate, H type steel, steel structure.
Rust removal: Rust removal of casting, forging, steel plate, H type steel, steel structure.
Sand blasting: Sand blasting of profile steel, ship board, steel board, steel material, steel structure.
Pre-treatment: Pre-treatment of surface, steel board, profile steel, steel structure, before painting or coating.
Related products
-
Steel Shot
Chemical Composition C 0.85-1.20% Si 0.40-1.20% Mn 0.60-1.20% S ≤0.05% P ≤0.05% Hardness HRC 40-50 Microstructure Homogeneous Tempered Martensite or Troostite Density ≥ 7.2g/cm3 External form Spherical Hollow particles<10% Size distribution Screen No. Inch Screen size S70 S110 S170 S230 S280 S330 S390 S460 S550 S660 S780 S930 6 0.132 3.35 ...
-
Sponge media abrasives
Sponge media abrasive is a cluster of abrasive media with urethane sponge as adhesive, which combines the containment capability of urethane sponge with the cleaning and cutting power of traditional blasting media. It flattens out during impact, exposing the abrasives to the surface with certain and profile created. When leaving the surface, the sponge expands back to regular size creating a vacuum which absorbs most of the contaminants, and therefore improves the sa...
-
Garnet
Features ■ Low Dust---The high intrinsic tenacity and a high proportion of the material itself fast the settlement rate and significantly reduce the dust emissions and dust coming from the workpiece, minimizing cleaning effort sandblasting, reducing pollution of the work area. ■ Excellent Surface Quality---It can deep into the voids and uneven parts to clean, thereby completely remove rust, soluble salts and other contaminants; surface blastin...
-
Bearing steel grit
Compared with traditional steel grit made by crushing steel shot, bearing steel grit has the following Features: Raw Material Bearing steel grit is made by Chromium bearing steel which has good harden ability due to its high content of Chromium. Technology Bearing steel grit is made by crushing the forged bearing steel directly which is free from casting defects. Low wear The forged state bearing steel grit with sharp edges has ...
-
Zinc cut wire
Made from high grade zinc wire, produced by cutting zinc wire into pellets, the length equal to the diameter of the wire. Zinc Cut Wire is also available in a conditioned form which is used as a longer lasting alternative to cast zinc shot. These are ideal for deflashing and finishing die castings, normally in wheel blast equipment. Available at competent rates, our products reduce wear and tear on blast equipment compared to most other metallic abrasives. ...
-
Aluminum cut wire
Aluminum cut wire shot also named as aluminum shot,aluminum beads, aluminum granules, aluminum pellet. It is made from superior quality aluminum wire, appearance is bright, is an ideal media for cleaning and reinforcing the surface of nonferrous metal casting parts. It's mainly applied for the surface treatment of Aluminum, Zinc products or work pieces with thin wall in shot blasting machine. Tech Data Products Alum...