18 Years Factory 430 0.5mm Stainless Steel Cut Wire Shot - Low Carbon Steel Shot – TAA
18 Years Factory 430 0.5mm Stainless Steel Cut Wire Shot - Low Carbon Steel Shot – TAA Detail:
Product feature
High strengthen, high tenacity, long service life.
Low breakage, low dust, low pollution.
Low wear of the equipments, long life of accessory.
Reduce dedusting system load, lengthen usage time of dedusting equipments.
Technical specification
|
Chemical Composition% |
C |
0.10-0.20% |
|
Si |
0.10-0.35% |
|
|
Mn |
0.35-1.50% |
|
|
S |
≤0.05% |
|
|
P |
≤0.05% |
|
|
Other alloy elements |
Adding Cr Mo Ni B Al Cu etc. |
|
|
Hardness |
HRC42-48/48-54 |
|
|
Microstructure |
Duplex structure combined Martensite and Bainite |
|
|
Density |
≥ 7.2g/cm3 |
|
|
External form |
Spherical |
|
Size distribution
| Screen No. | Inch | Screen size | S70 | S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
| 6 | 0.132 | 3.35 | All pass | |||||||||||
| 7 | 0.111 | 2.80 | All pass | |||||||||||
| 8 | 0.0937 | 2.36 | All pass | ≥90% | ||||||||||
| 10 | 0.0787 | 2.00 | All pass | All pass | ≥85% | ≥97% | ||||||||
| 12 | 0.0661 | 1.70 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 14 | 0.0555 | 1.40 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 16 | 0.0469 | 1.18 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 18 | 0.0394 | 1.00 | All pass | ≤5% | ≥85% | ≥96% | ||||||||
| 20 | 0.0331 | 0.850 | All pass | ≤10% | ≥85% | ≥96% | ||||||||
| 25 | 0.0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
| 30 | 0.0232 | 0.600 | All pass | ≥85% | ≥96% | |||||||||
| 35 | 0.0197 | 0.500 | ≤10% | ≥97% | ||||||||||
| 40 | 0.0165 | 0.425 | All Pass | ≥85% | ||||||||||
| 45 | 0.0138 | 0.355 | ≤10% | ≥97% | ||||||||||
| 50 | 0.0117 | 0.300 | ≥80% | |||||||||||
| 80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
| 120 | 0.0049 | 0.125 | ≥90% | |||||||||||
| 200 | 0.0029 | 0.075 |
Fatigue Life Test
Consumption Contrast Figure of TAA LCB steel shot, low-carbon steel shot and high-carbon steel shot.(fatigue life test of normal grades at an impacting speed ratio of 60.96m/s)
Consumption contrast-Normal grade
Through the fatigue life test we can see that: the service life of TAA LCB Steel Shot is 1.5 times longer than common low carbon steel shot, 2 times longer than high carbon steel shot.
Application
Blast cleaning: Used for blast cleaning of casting, die-casting, forging; sand removal of casting, steel plate, H type steel, steel structure.
Rust removal: Rust removal of casting, forging, steel plate, H type steel, steel structure.
Shot peening: Shot peening of gear, heat treated parts.
Sand blasting: Sand blasting of profile steel, ship board, steel board, steel material, steel structure.
Pre-treatment: Pre-treatment of surface, steel board, profile steel, steel structure, before painting or coating.
Product detail pictures:
Related Product Guide:
We now have a specialist, efficiency workforce to deliver excellent service for our purchaser. We always follow the tenet of customer-oriented, details-focused for 18 Years Factory 430 0.5mm Stainless Steel Cut Wire Shot - Low Carbon Steel Shot – TAA , The product will supply to all over the world, such as: Cairo, India, Zurich, By integrating manufacturing with foreign trade sectors, we can provide total customer solutions by guaranteeing the delivery of right products to the right place at the right time, which is supported by our abundant experiences, powerful production capability, consistent quality, diversified product portfolios and the control of the industry trend as well as our mature before and after sales services. We'd like to share our ideas with you and welcome your comments and questions.
By Alice from Uruguay - 2018.04.25 16:46
A good manufacturers, we have cooperated twice, good quality and good service attitude.
By Eve from Libya - 2017.06.22 12:49
Related products
-
Cheap price Stainless Steel Cut Wire Shot Sus43...
Features * Can be used to replace a variety of mineral sands & non-metallic abrasives,such as corundum, silicon carbide, arenaceous quartz, glass beads, etc. * Low dust emissions,improving operating environment, environmental friendly. * Can replace part of the pickling process. * Low dust emission and excellent operating environment, reducing the treatment of pickling waste. * Low comprehensive cost, the service life is 30-100 times that of non-metallic abrasive such as corundum. * Can B...
-
Good Wholesale Vendors Brown Fused Alumina Dens...
Chemical Composition C 0.85-1.20% Si 0.40-1.20% Mn 0.60-1.20% S ≤0.05% P ≤0.05% Hardness HRC 40-50 Microstructure Homogeneous Tempered Martensite or Troostite Density ≥ 7.2g/cm3 External form Spherical Hollow particles<10% Size distribution Screen No. Inch Screen size S70 S110 S170 S230 S280 S330 S390 S460 S550 S660 S780 S930 6 0.132 3.35 All pass 7 0.111 2.80 All pass 8 0.0937 2.36 All pass ≥90% 10 0.0787 2.00 All pa...
-
Good User Reputation for Bearing Steel Grit - ...
Aluminum cut wire shot also named as aluminum shot,aluminum beads, aluminum granules, aluminum pellet. It is made from superior quality aluminum wire, appearance is bright, is an ideal media for cleaning and reinforcing the surface of nonferrous metal casting parts. It’s mainly applied for the surface treatment of Aluminum, Zinc products or work pieces with thin wall in shot blasting machine. Tech Data Products Aluminium Cut Wire Shot Chemical Composition Al≥99% Microhar...
-
Original Factory 0.3mm Zinc Cut Wire - Steel G...
Available Hardness: GP: HRC46-50 Newly made products with angular, the grit are gradually rounded off in use and its particularly suited for oxide skin pre-treatment. GL: HRC56-60 Harder than GP steel grit, also loses its sharp edges during shot basting and is particularly suited to surface preparation applications. GH: HRC63-65 High hardness, sharp edges remain during operation, mainly used for compressed air shot blasting equipment. Production Strength: TAA adopts Arc Furnace Smelting an...
-
China Supplier Glass Bead Blasting 60 Grit - G...
Features ■ Low Dust—The high intrinsic tenacity and a high proportion of the material itself fast the settlement rate and significantly reduce the dust emissions and dust coming from the workpiece, minimizing cleaning effort sandblasting, reducing pollution of the work area. ■ Excellent Surface Quality—It can deep into the voids and uneven parts to clean, thereby completely remove rust, soluble salts and other contaminants; surface blasting process without inserts, will not a...
-
Best Price for Thermal Conductivity Brown Fused...
Available Hardness: GP: HRC46-50 Newly made products with angular, the grit are gradually rounded off in use and its particularly suited for oxide skin pre-treatment. GL: HRC56-60 Harder than GP steel grit, also loses its sharp edges during shot basting and is particularly suited to surface preparation applications. GH: HRC63-65 High hardness, sharp edges remain during operation, mainly used for compressed air shot blasting equipment. Production Strength: TAA adopts Arc Furnace Smelting an...