factory customized Stainless Steel Shot Blasting Machine - Steel Shot – TAA
factory customized Stainless Steel Shot Blasting Machine - Steel Shot – TAA Detail:
| Chemical Composition | C | 0.85-1.20% |
| Si | 0.40-1.20% | |
| Mn | 0.60-1.20% | |
| S | ≤0.05% | |
| P | ≤0.05% | |
| Hardness | HRC 40-50 | |
| Microstructure | Homogeneous Tempered Martensite or Troostite | |
| Density | ≥ 7.2g/cm3 | |
| External form | Spherical Hollow particles<10% |
|
Size distribution
| Screen No. | Inch | Screen size | S70 | S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
| 6 | 0.132 | 3.35 | All pass | |||||||||||
| 7 | 0.111 | 2.80 | All pass | |||||||||||
| 8 | 0.0937 | 2.36 | All pass | ≥90% | ||||||||||
| 10 | 0.0787 | 2.00 | All pass | All pass | ≥85% | ≥97% | ||||||||
| 12 | 0.0661 | 1.70 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 14 | 0.0555 | 1.40 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 16 | 0.0469 | 1.18 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 18 | 0.0394 | 1.00 | All pass | ≤5% | ≥85% | ≥96% | ||||||||
| 20 | 0.0331 | 0.850 | All pass | ≤10% | ≥85% | ≥96% | ||||||||
| 25 | 0.0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
| 30 | 0.0232 | 0.600 | All pass | ≥85% | ≥96% | |||||||||
| 35 | 0.0197 | 0.500 | ≤10% | ≥97% | ||||||||||
| 40 | 0.0165 | 0.425 | All Pass | ≥85% | ||||||||||
| 45 | 0.0138 | 0.355 | ≤10% | ≥97% | ||||||||||
| 50 | 0.0117 | 0.300 | ≥80% | |||||||||||
| 80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
| 120 | 0.0049 | 0.125 | ≥90% | |||||||||||
| 200 | 0.0029 | 0.075 |
Application
Blast cleaning: Used for blast cleaning of casting, die-casting, forging; sand removal of casting, steel plate, H type steel, steel structure.
Rust removal: Rust removal of casting, forging, steel plate, H type steel, steel structure.
Shot peening: Shot peening of gear, heat treated parts.
Sand blasting: Sand blasting of profile steel, ship board, steel board, steel material, steel structure.
Pre-treatment: Pre-treatment of surface, steel board, profile steel, steel structure, before painting or coating.
Product detail pictures:
Related Product Guide:
To be the stage of realizing dreams of our employees! To build a happier, more united and more professional team! To reach a mutual benefit of our customers, suppliers, the society and ourselves for factory customized Stainless Steel Shot Blasting Machine - Steel Shot – TAA , The product will supply to all over the world, such as: United Kingdom, Bangladesh, France, Based on our automatic production line, steady material purchase channel and quick subcontract systems have been built in mainland China to meet customer's wider and higher requirement in recent years. We are looking forward to cooperating with more clients worldwide for common development and mutual benefit!Your trust and approval are the best reward for our efforts. Keeping honest, innovative and efficient, we sincerely expect that we can be business partners to create our brilliant future!
By Constance from Saudi Arabia - 2017.05.21 12:31
This company has a lot of ready-made options to choose and also could custom new program according to our demand, which is very nice to meet our needs.
By Alex from Islamabad - 2018.02.08 16:45
Related products
-
Reasonable price Copper Cut Wire Blast Media -...
Features ■ Low Dust—The high intrinsic tenacity and a high proportion of the material itself fast the settlement rate and significantly reduce the dust emissions and dust coming from the workpiece, minimizing cleaning effort sandblasting, reducing pollution of the work area. ■ Excellent Surface Quality—It can deep into the voids and uneven parts to clean, thereby completely remove rust, soluble salts and other contaminants; surface blasting process without inserts, will not a...
-
Wholesale blasting glass bead - Copper cut wir...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass beads 5. Sh...
-
Cheapest Price Nesco Shot Blasting Machine - B...
Available Spare parts materials Content of Cr-12%, 20%, 25% or as request. Product Features Advanced & scientific precision casting Process and technology . High efficiency and automatic single station drying production line. Special high chromium abrasion casting iron spare parts, making up gaps in the domestic industry. Original Equipment Manufactured (OEM) parts are available. We also offer quality aftermarket parts for other brand machines.
-
New Arrival China 2.0mm Copper Cut Wire Shot -...
Product feature High strengthen, high tenacity, long service life. Low breakage, low dust, low pollution. Low wear of the equipments, long life of accessory. Reduce dedusting system load, lengthen usage time of dedusting equipments. Technical specification Chemical Composition% C 0.10-0.20% Si 0.10-0.35% Mn 0.35-1.50% S ≤0.05% P ≤0.05% Other alloy elements Adding Cr Mo Ni B Al Cu etc. Hardness HRC42-48/48-54 Microstructure Duple...
-
Fixed Competitive Price Glass Bead Blasting Med...
Chemical Composition C 0.85-1.20% Si 0.40-1.20% Mn 0.60-1.20% S ≤0.05% P ≤0.05% Hardness HRC 40-50 Microstructure Homogeneous Tempered Martensite or Troostite Density ≥ 7.2g/cm3 External form Spherical Hollow particles<10% Size distribution Screen No. Inch Screen size S70 S110 S170 S230 S280 S330 S390 S460 S550 S660 S780 S930 6 0.132 3.35 All pass 7 0.111 2.80 All pass 8 0.0937 2.36 All...
-
Quality Inspection for Sponge Jet Blasting - L...
Product feature High strengthen, high tenacity, long service life. Low breakage, low dust, low pollution. Low wear of the equipments, long life of accessory. Reduce dedusting system load, lengthen usage time of dedusting equipments. Technical specification Chemical Composition% C 0.10-0.20% Si 0.10-0.35% Mn 0.35-1.50% S ≤0.05% P ≤0.05% Other alloy elements Adding Cr Mo Ni B Al Cu etc. Hardness HRC42-48/48-54 Microstructure Duplex structure co...