High Quality Gl14 Bearing Steel Grit - Stainless steel cut wire shot – TAA
High Quality Gl14 Bearing Steel Grit - Stainless steel cut wire shot – TAA Detail:
Stainless steel cut wire shot is widely used for the shot/air blasting of various types of non-ferrous metal castings, stainless steel products, aluminum parts, hardware tools, natural stone, etc, highlighting the metal color and achieving smooth, rust-free, matt fi nishing surface treatment eff ect. With good quality stainless steel wire raw material, stainless steel shot is featured with uniform particles and hardness, which guarantees its long service life and good blasting eff ect. The pellets after conditioning have low wear to the blasting machines.
Stainless steel cut wire
Stainless steel cut wire G1
Stainless steel cut wire G2
Stainless steel cut wire G3
Stainless steel cut wire-As cut, cylindrical
G1 Shape-After the treatment for cut surface’s edges, to get the edges passivated
G2 Shape-Semi conditioned
G3 Shape-Get rid of all the edges to make it become ball type, almost spherical
Technical specification
|
SUS304 |
SUS430 |
SUS410 |
|||||
|
Chemical Composition |
C |
≤0.08% |
≤0.12% |
≤0.15% |
|||
|
Si |
≤1.00% |
≤1.00% |
≤1.00% |
||||
|
Mn |
≤2.00% |
≤1.00% |
≤1.00% |
||||
|
S |
≤0.030% |
≤0.030% |
≤0.030% |
||||
|
P |
≤0.045% |
≤0.040% |
≤0.040% |
||||
|
Cr |
18-20% |
16-18% |
11.5-13.5% |
||||
|
Ni |
8-11% |
/ |
/ |
||||
|
Hardness |
HRC38-52 |
HRC25-35 |
HRC20-30 |
||||
|
External form |
Cylindrical/Spherical |
||||||
|
Microstructure |
Austenitic |
Ferrite |
Deformed martensite |
||||
|
Density |
≥7.80g/cm3 |
||||||
Advantages
Produces with very bright surfaces
Dust free surfaces and lower dust when blasting
Longer life than cast abrasives and carbon cut wire shot
No ferrous contamination
No hollow,splits or twins
Available “as cut” or “conditioned”
Available sizes: 0.3mm,0.4mm,0.5mm,0.6mm,0.8mm,1.0mm,1.2mm,1.4mm, 1.5mm
Packing: 25kgs/bag,40bags/wooden pallet or as request.
Product detail pictures:
Related Product Guide:
In the past few years, our company absorbed and digested advanced technologies both at home and abroad. Meanwhile, our company staffs a team of experts devoted to the development of High Quality Gl14 Bearing Steel Grit - Stainless steel cut wire shot – TAA , The product will supply to all over the world, such as: Thailand, European, Rwanda, With excellent solutions, high quality service and sincere attitude of service, we ensure customer satisfaction and help customers create value for mutual benefit and create a win-win situation. Welcome customers all over the world to contact us or visit our company. We'll satisfy you with our qualified service!
By Melissa from Jakarta - 2018.09.23 18:44
Reasonable price, good attitude of consultation, finally we achieve a win-win situation,a happy cooperation!
By Martina from Jamaica - 2018.09.23 17:37
Related products
-
Leading Manufacturer for Aluminum Oxide Fused -...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass beads 5. Sh...
-
Professional China Metal Grinding Disc - Cutti...
Our super-hard alloy tools are produced by brazing. Under certain conditions, a layer of diamond is firmly welded to the metal substrate after a metal solder melting process. This type of product has the characteristics of high grinding efficiency, long service life, safety, environmental protection and pollution-free. Mainly replace the current resin bond corundum cutting and polishing tools, all coarse and medium coarse-grained electroplated diamond tools, and some hot-pressed sintered diam...
-
Factory best selling Abrasive Grit Garnet - Ca...
We made great improvement in material and the techniques on the basis of the traditional production process. Utilizing high quality alloy steel wire as the substrate that higher the mechanical properties and make it more stable. Improving the wiredrawing craft which make the internal organization more dense. Improving the traditional passivation process that completely relying on impacting to reduce the damage during blasting, enhancing the service life. Item Technical index Chemi...
-
Best quality Steel Grit Gp14 - Steel Grit R...
Available Hardness: GP: HRC46-50 Newly made products with angular, the grit are gradually rounded off in use and its particularly suited for oxide skin pre-treatment. GL: HRC56-60 Harder than GP steel grit, also loses its sharp edges during shot basting and is particularly suited to surface preparation applications. GH: HRC63-65 High hardness, sharp edges remain during operation, mainly used for compressed air shot blasting equipment. Production Strength: TAA adopts Arc Furnace Smelting an...
-
professional factory for 1.2mm Zinc Cut Wire -...
Made from high grade zinc wire, produced by cutting zinc wire into pellets, the length equal to the diameter of the wire. Zinc Cut Wire is also available in a conditioned form which is used as a longer lasting alternative to cast zinc shot. These are ideal for deflashing and finishing die castings, normally in wheel blast equipment. Available at competent rates, our products reduce wear and tear on blast equipment compared to most other metallic abrasives. Features 1. Bright colour and lustre...
-
Good quality Diamond Cup Grinding Disc - Cutti...
Our super-hard alloy tools are produced by brazing. Under certain conditions, a layer of diamond is firmly welded to the metal substrate after a metal solder melting process. This type of product has the characteristics of high grinding efficiency, long service life, safety, environmental protection and pollution-free. Mainly replace the current resin bond corundum cutting and polishing tools, all coarse and medium coarse-grained electroplated diamond tools, and some hot-pressed sintered diam...