Product feature
High strengthen, high tenacity, long service life.
Low breakage, low dust, low pollution.
Low wear of the equipments, long life of accessory.
Reduce dedusting system load, lengthen usage time of dedusting equipments.
Technical specification
|
Chemical Composition% |
C |
0.10-0.20% |
|
Si |
0.10-0.35% |
|
|
Mn |
0.35-1.50% |
|
|
S |
≤0.05% |
|
|
P |
≤0.05% |
|
|
Other alloy elements |
Adding Cr Mo Ni B Al Cu etc. |
|
|
Hardness |
HRC42-48/48-54 |
|
|
Microstructure |
Duplex structure combined Martensite and Bainite |
|
|
Density |
≥ 7.2g/cm3 |
|
|
External form |
Spherical |
|
Size distribution
| Screen No. | Inch | Screen size | S70 | S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
| 6 | 0.132 | 3.35 | All pass | |||||||||||
| 7 | 0.111 | 2.80 | All pass | |||||||||||
| 8 | 0.0937 | 2.36 | All pass | ≥90% | ||||||||||
| 10 | 0.0787 | 2.00 | All pass | All pass | ≥85% | ≥97% | ||||||||
| 12 | 0.0661 | 1.70 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 14 | 0.0555 | 1.40 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 16 | 0.0469 | 1.18 | All pass | ≤5% | ≥85% | ≥97% | ||||||||
| 18 | 0.0394 | 1.00 | All pass | ≤5% | ≥85% | ≥96% | ||||||||
| 20 | 0.0331 | 0.850 | All pass | ≤10% | ≥85% | ≥96% | ||||||||
| 25 | 0.0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
| 30 | 0.0232 | 0.600 | All pass | ≥85% | ≥96% | |||||||||
| 35 | 0.0197 | 0.500 | ≤10% | ≥97% | ||||||||||
| 40 | 0.0165 | 0.425 | All Pass | ≥85% | ||||||||||
| 45 | 0.0138 | 0.355 | ≤10% | ≥97% | ||||||||||
| 50 | 0.0117 | 0.300 | ≥80% | |||||||||||
| 80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
| 120 | 0.0049 | 0.125 | ≥90% | |||||||||||
| 200 | 0.0029 | 0.075 |
Fatigue Life Test
Consumption Contrast Figure of TAA LCB steel shot, low-carbon steel shot and high-carbon steel shot.(fatigue life test of normal grades at an impacting speed ratio of 60.96m/s)
Consumption contrast-Normal grade
Through the fatigue life test we can see that: the service life of TAA LCB Steel Shot is 1.5 times longer than common low carbon steel shot, 2 times longer than high carbon steel shot.
Application
Blast cleaning: Used for blast cleaning of casting, die-casting, forging; sand removal of casting, steel plate, H type steel, steel structure.
Rust removal: Rust removal of casting, forging, steel plate, H type steel, steel structure.
Shot peening: Shot peening of gear, heat treated parts.
Sand blasting: Sand blasting of profile steel, ship board, steel board, steel material, steel structure.
Pre-treatment: Pre-treatment of surface, steel board, profile steel, steel structure, before painting or coating.
Product detail pictures:
Related Product Guide:
That has a sound small business credit, great after-sales service and modern production facilities, we've earned an outstanding standing amid our buyers across the earth for Hot sale Garnet Abrasive Blasting - Low Carbon Steel Shot – TAA , The product will supply to all over the world, such as: Las Vegas, Azerbaijan, Liverpool, Our products are exported worldwide. Our customers are always satisfied with our reliable quality, customer-oriented services and competitive prices. Our mission is "to continue to earn your loyalty by dedicating our efforts to the constant improvement of our products and services in order to ensure the satisfaction of our end-users, customers, employees, suppliers and the worldwide communities in which we cooperate".
By Constance from Accra - 2018.06.18 19:26
High Quality, High Efficiency, Creative and Integrity, worth having long-term cooperation! Looking forward to the future cooperation!
By Ella from United Kingdom - 2018.06.30 17:29
Related products
-
Factory Cheap Hot Bearing Steel Grit Gh25 - Ga...
Features ■ Low Dust—The high intrinsic tenacity and a high proportion of the material itself fast the settlement rate and significantly reduce the dust emissions and dust coming from the workpiece, minimizing cleaning effort sandblasting, reducing pollution of the work area. ■ Excellent Surface Quality—It can deep into the voids and uneven parts to clean, thereby completely remove rust, soluble salts and other contaminants; surface blasting process without inserts, will not a...
-
Best Price on Steel Shot Shot Peening - Steel ...
Available Hardness: GP: HRC46-50 Newly made products with angular, the grit are gradually rounded off in use and its particularly suited for oxide skin pre-treatment. GL: HRC56-60 Harder than GP steel grit, also loses its sharp edges during shot basting and is particularly suited to surface preparation applications. GH: HRC63-65 High hardness, sharp edges remain during operation, mainly used for compressed air shot blasting equipment. Production Strength: TAA adopts Arc Furnace Smelting an...
-
Special Price for Manual Shot Blasting Machine ...
Important Advantages AGTOS blasting technology: Our turbines are strong power units which are highly cost-effective due to fewer wear parts and a high abrasive flfl ow. Easy to maintain The innovative filtering technology convinces through strong performances. Automation Blasting of flfl ame cut pieces in a basket Blasting machine with adjustable passage height Bar blasting machine Blast machine for metal sheets, sections and constructions with a passage height of up to 1000 m Diabolo b...
-
2018 China New Design Copper Cut Wire - Copper...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass beads 5. Sh...
-
Best Price for 304 0.4mm Stainless Steel Cut Wi...
Features Alumina oxide abrasive have high hardness and sharp angular, is widely used for both wet and dry blasting, creating the suitable profile for surface preparation. Alumina oxide abrasive is an idea blasting abrasive media for surface preparation requesting ferrous free. Alumina oxide abrasive is high efficiency blasting abrasives with sharp edges and high density. It is reusable and can be used in different types of blasting machine. Technical specification Type Item Appearance A...
-
Hot sale Factory Stainless Steel Shot Hs Code -...
Compared with traditional steel grit made by crushing steel shot, bearing steel grit has the following Features: Raw Material Bearing steel grit is made by Chromium bearing steel which has good harden ability due to its high content of Chromium. Technology Bearing steel grit is made by crushing the forged bearing steel directly which is free from casting defects. Low wear The forged state bearing steel grit with sharp edges has higher mechanical property than traditional cast steel grit with...