Manufacturer of G18 Sponge Media Abrasives - Stainless steel cut wire shot – TAA
Manufacturer of G18 Sponge Media Abrasives - Stainless steel cut wire shot – TAA Detail:
Stainless steel cut wire shot is widely used for the shot/air blasting of various types of non-ferrous metal castings, stainless steel products, aluminum parts, hardware tools, natural stone, etc, highlighting the metal color and achieving smooth, rust-free, matt fi nishing surface treatment eff ect. With good quality stainless steel wire raw material, stainless steel shot is featured with uniform particles and hardness, which guarantees its long service life and good blasting eff ect. The pellets after conditioning have low wear to the blasting machines.
Stainless steel cut wire
Stainless steel cut wire G1
Stainless steel cut wire G2
Stainless steel cut wire G3
Stainless steel cut wire-As cut, cylindrical
G1 Shape-After the treatment for cut surface’s edges, to get the edges passivated
G2 Shape-Semi conditioned
G3 Shape-Get rid of all the edges to make it become ball type, almost spherical
Technical specification
|
SUS304 |
SUS430 |
SUS410 |
|||||
|
Chemical Composition |
C |
≤0.08% |
≤0.12% |
≤0.15% |
|||
|
Si |
≤1.00% |
≤1.00% |
≤1.00% |
||||
|
Mn |
≤2.00% |
≤1.00% |
≤1.00% |
||||
|
S |
≤0.030% |
≤0.030% |
≤0.030% |
||||
|
P |
≤0.045% |
≤0.040% |
≤0.040% |
||||
|
Cr |
18-20% |
16-18% |
11.5-13.5% |
||||
|
Ni |
8-11% |
/ |
/ |
||||
|
Hardness |
HRC38-52 |
HRC25-35 |
HRC20-30 |
||||
|
External form |
Cylindrical/Spherical |
||||||
|
Microstructure |
Austenitic |
Ferrite |
Deformed martensite |
||||
|
Density |
≥7.80g/cm3 |
||||||
Advantages
Produces with very bright surfaces
Dust free surfaces and lower dust when blasting
Longer life than cast abrasives and carbon cut wire shot
No ferrous contamination
No hollow,splits or twins
Available “as cut” or “conditioned”
Available sizes: 0.3mm,0.4mm,0.5mm,0.6mm,0.8mm,1.0mm,1.2mm,1.4mm, 1.5mm
Packing: 25kgs/bag,40bags/wooden pallet or as request.
Product detail pictures:
Related Product Guide:
Our solutions are widely regarded and trustworthy by consumers and may meet continually modifying financial and social requirements for Manufacturer of G18 Sponge Media Abrasives - Stainless steel cut wire shot – TAA , The product will supply to all over the world, such as: Chile, Grenada, Mauritania, we rely on own advantages to build a mutual-benefit commerce mechanism with our cooperative partners. As a result, now we have gained a global sales network reaching the Middle East, Turkey, Malaysia and Vietnamese.
By Marcy Real from Bogota - 2018.02.21 12:14
The sales manager is very patient, we communicated about three days before we decided to cooperate, finally, we are very satisfied with this cooperation!
By Anne from Australia - 2017.08.15 12:36
Related products
-
PriceList for Glass Bead For Blasting - Sponge...
Sponge Media abrasive are available in over 20 types,achieving profiles from 0 to 100+ micron. All procides dry, low dust, low rebound blasting. The most commomly used is TAA-S series with aluminum oxide and TAA-G series with steel grit. Type Profiles Abrasive Media Agent Application TAA-S#16 ±100 micron Aluminum Oxide#16 Fast and aggressive for tough industrial coatings. TAA-S#30 ±75 micron Aluminum Oxide#30 Removal of multilayer coatings and profile to 75 micron. TAA-S#30 ±50 micro...
-
Factory wholesale S110 Low Carbon Steel Shot -...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass beads 5. Sh...
-
Factory Outlets Cutting Disc In Face - Grindin...
Our super-hard alloy tools are produced by brazing. Under certain conditions, a layer of diamond is firmly welded to the metal substrate after a metal solder melting process. This type of product has the characteristics of high grinding efficiency, long service life, safety, environmental protection and pollution-free. Mainly replace the current resin bond corundum cutting and polishing tools, all coarse and medium coarse-grained electroplated diamond tools, and some hot-pressed sintered diam...
-
Fixed Competitive Price 2.0mm Aluminum Cut Wire...
Advantage ■ clean and smooth, not hurt to the mechanical precision of work piece. ■ high mechanical intensity, hardness, flexibility ■ it can be reused several times, the same effect and is not easily broken. ■ uniform size, after blasting sand around the device to maintain a uniform brightness effect, not easy to leave a watermark. ■ high purity and good quality meet the international standard. ■ stable chemistry property, not pollute the metal processed. Technical specificatio...
-
China Factory for 120# Brown Fused Alumina - C...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass beads 5. Sh...
-
New Arrival China 2.0mm Copper Cut Wire Shot -...
Product feature High strengthen, high tenacity, long service life. Low breakage, low dust, low pollution. Low wear of the equipments, long life of accessory. Reduce dedusting system load, lengthen usage time of dedusting equipments. Technical specification Chemical Composition% C 0.10-0.20% Si 0.10-0.35% Mn 0.35-1.50% S ≤0.05% P ≤0.05% Other alloy elements Adding Cr Mo Ni B Al Cu etc. Hardness HRC42-48/48-54 Microstructure Duplex structure co...