Chinese Professional Garnet Sandblast Media - Aluminum cut wire – TAA Detail:
Aluminum cut wire shot also named as aluminum shot,aluminum beads, aluminum granules, aluminum pellet. It is made from superior quality aluminum wire, appearance is bright, is an ideal media for cleaning and reinforcing the surface of nonferrous metal casting parts. It’s mainly applied for the surface treatment of Aluminum, Zinc products or work pieces with thin wall in shot blasting machine.
Tech Data
|
Products |
Aluminium Cut Wire Shot |
|
Chemical Composition |
Al≥99% |
|
Microhardness |
45~50HV |
|
Tensile Intensity |
80~240Mpa |
|
Durability |
6500 Times |
|
Microstructure |
Deformed α |
|
Density |
2.7g/cm3 |
|
Bulk Density |
1.5g/cm3 |
|
Appearance |
cylindrical |
Available sizes: 0.6mm, 0.8mm, 1.0mm, 1.2mm, 1.5mm, 2.0mm, 2.5mm
Advantages
■ Most economical and lowest consumption
■ Consumption 3-4 times less compare to cast shot
■ No dust formation
■ Faster cleaning
■ Environmental friendly
■ Uniform hardness
■ Stabilized grain size
■ Increased fatigue life of blasted part
Appearance: As-cut(cylindrical)
Application
Surface cleaning and rust removing for cast iron, cast steel, steel plates and steel pipes, metal die casting; precision casting; hardware machinery manufacturing; auto instrumentation, derusting, intensifying, smoothing and so on. Especially used in shot blasting machine and peening machine.
Application
Surface cleaning and rust removing for cast iron, cast steel, steel plates and steel pipes, especially used in shot blasting machine and peening machine.
Product detail pictures:
Related Product Guide:
"Based on domestic market and expand overseas business" is our improvement strategy for Chinese Professional Garnet Sandblast Media - Aluminum cut wire – TAA , The product will supply to all over the world, such as: Paraguay, Czech republic, Uganda, Our company offers the full range from pre-sales to after-sales service, from product development to audit the use of maintenance, based on strong technical strength, superior product performance, reasonable prices and perfect service, we'll continue to develop, to deliver the high-quality items and services, and promote lasting cooperation with our customers, common development and create a better future.
By Lena from Oman - 2017.01.28 19:59
The after-sale warranty service is timely and thoughtful, encounter problems can be resolved very quickly, we feel reliable and secure.
By Georgia from Albania - 2018.06.28 19:27
Related products
-
Chinese Professional Stainless Steel Grit - Be...
Compared with traditional steel grit made by crushing steel shot, bearing steel grit has the following Features: Raw Material Bearing steel grit is made by Chromium bearing steel which has good harden ability due to its high content of Chromium. Technology Bearing steel grit is made by crushing the forged bearing steel directly which is free from casting defects. Low wear The forged state bearing steel grit with sharp edges has higher mechanical property than traditional cast steel gr...
-
OEM/ODM China Bearing Steel Grit Gh80 - Garnet...
Features ■ Low Dust—The high intrinsic tenacity and a high proportion of the material itself fast the settlement rate and significantly reduce the dust emissions and dust coming from the workpiece, minimizing cleaning effort sandblasting, reducing pollution of the work area. ■ Excellent Surface Quality—It can deep into the voids and uneven parts to clean, thereby completely remove rust, soluble salts and other contaminants; surface blasting process without inserts, will not advers...
-
18 Years Factory 430 0.5mm Stainless Steel Cut ...
Product feature High strengthen, high tenacity, long service life. Low breakage, low dust, low pollution. Low wear of the equipments, long life of accessory. Reduce dedusting system load, lengthen usage time of dedusting equipments. Technical specification Chemical Composition% C 0.10-0.20% Si 0.10-0.35% Mn 0.35-1.50% S ≤0.05% P ≤0.05% Other alloy elements Adding Cr Mo Ni B Al Cu etc. Hardness HRC42-48/48-54 Microstructure Duplex structure co...
-
New Fashion Design for Brown Fused Alumina Mark...
Product feature High strengthen, high tenacity, long service life. Low breakage, low dust, low pollution. Low wear of the equipments, long life of accessory. Reduce dedusting system load, lengthen usage time of dedusting equipments. Technical specification Chemical Composition% C 0.10-0.20% Si 0.10-0.35% Mn 0.35-1.50% S ≤0.05% P ≤0.05% Other alloy elements Adding Cr Mo Ni B Al Cu etc. Hardness HRC42-48/48-54 Microstructure Duple...
-
Factory Cheap Cast Zinc Shot - Copper cut wire...
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific gravity higher than other blasting beads 4. Lower hardness than steel shot &glass beads 5. Sh...
-
Good User Reputation for Replacement Grinding W...
Our super-hard alloy tools are produced by brazing. Under certain conditions, a layer of diamond is firmly welded to the metal substrate after a metal solder melting process. This type of product has the characteristics of high grinding efficiency, long service life, safety, environmental protection and pollution-free. Mainly replace the current resin bond corundum cutting and polishing tools, all coarse and medium coarse-grained electroplated diamond tools, and some hot-pressed sintered diam...