Zinc cut wire
Made from high grade zinc wire, produced by cutting zinc wire into pellets, the length equal to the diameter of the wire. Zinc Cut Wire is also available in a conditioned form which is used as a longer lasting alternative to cast zinc shot.
These are ideal for deflashing and finishing die castings, normally in wheel blast equipment. Available at competent rates, our products reduce wear and tear on blast equipment compared to most other metallic abrasives.
Features
1. Bright colour and lustre
2. Compact structure
3. Little impurity and high purity
4. No premature breakdown or flaking
5. Less dust than either steel or aluminum abrasives
6. Durability: 6500 times
Technological Index
|
Product Description |
Zinc Cut Wire Shot |
|
Chemical Composition |
Zn≥99.9% |
|
Microhardness |
35~45HV |
|
Tensile Intensity |
90~120Mpa |
|
Durability |
6500 Times |
|
Microstructure |
Deformed α |
|
Density |
7.1 g/cm3 |
|
Bulk Density |
4.1g/cm3 |
|
Hardness |
As cut:38-55HV Conditioned:45-60HV |
Available sizes
1. Zinc cut wire: 1.5mm 1.8mm 2.0mm 2.5mm 3.0mm
2. Zinc Shot: 0.3mm 0.4mm 0.5mm 0.6mm 0.8mm
Shapes: As cut(cylindrical), conditioned(rounded)
Application
It is used for removing oxidation skin, burr, eliminating surface defect, removing stress, etching, strengthen, prevention rust before painting of metal die-casting, precision casting, hardware tool, machinery manufacturing, automobile spare parts, apparatus and pump valves.
Related products
-
Brown Fused Alumina
Features Alumina oxide abrasive have high hardness and sharp angular, is widely used for both wet and dry blasting, creating the suitable profile for surface preparation. Alumina oxide abrasive is an idea blasting abrasive media for surface preparation requesting ferrous free. Alumina oxide abrasive is high efficiency blasting abrasives with sharp edges and high density. It is reusable and can be used in different types of blasting machine. ...
-
Steel Shot
Chemical Composition C 0.85-1.20% Si 0.40-1.20% Mn 0.60-1.20% S ≤0.05% P ≤0.05% Hardness HRC 40-50 Microstructure Homogeneous Tempered Martensite or Troostite Density ≥ 7.2g/cm3 External form Spherical Hollow particles<10% Size distribution Screen No. Inch Screen size S70 S110 S170 S230 S280 S330 S390 S460 S550 S660 S780 S930 6 0.132 3.35 ...
-
Garnet
Features ■ Low Dust---The high intrinsic tenacity and a high proportion of the material itself fast the settlement rate and significantly reduce the dust emissions and dust coming from the workpiece, minimizing cleaning effort sandblasting, reducing pollution of the work area. ■ Excellent Surface Quality---It can deep into the voids and uneven parts to clean, thereby completely remove rust, soluble salts and other contaminants; surface blastin...
-
Stainless steel grit
Features * Can be used to replace a variety of mineral sands & non-metallic abrasives,such as corundum, silicon carbide, arenaceous quartz, glass beads, etc. * Low dust emissions,improving operating environment, environmental friendly. * Can replace part of the pickling process. * Low dust emission and excellent operating environment, reducing the treatment of pickling waste. * Low comprehensive cost, the service life is 30-100 times that ...
-
Copper cut wire
Tech Data Product Description Copper Cut Wire Shot Chemical Composition Cu: 58-99%, the rest is Zn Microhardness 110~300HV Tensile Intensity 200~500Mpa Durability 5000 Times Microstructure Deformed αorα+β Density 8.9 g/cm3 Bulk Density 5.1 g/cm3 Available sizes: 1.0mm, 1.5mm, 2.0mm, 2.5mm etc. Advantage 1. Long life time 2. Less Dust 3. Specific g...
-
Sponge media abrasives
Sponge media abrasive is a cluster of abrasive media with urethane sponge as adhesive, which combines the containment capability of urethane sponge with the cleaning and cutting power of traditional blasting media. It flattens out during impact, exposing the abrasives to the surface with certain and profile created. When leaving the surface, the sponge expands back to regular size creating a vacuum which absorbs most of the contaminants, and therefore improves the sa...